| Grade : | 1.4104马氏体不锈钢 | |||||
| Number: | X14CrMoS17 | |||||
| Classification: | 马氏体不锈钢 | |||||
| Density: | 7.7 g/cm 3 | |||||
| Standard: | ||||||
| EN 10088-3:2005不锈钢。一般用途耐腐蚀钢的半成品、棒材、线材、型材和光亮产品的交货技术条件 | ||||||
| EN 10088-1:2005不锈钢。不锈钢清单 | ||||||
| Equivalent grades: | ||||||
| Chemical composition % of steel X14CrMoS17 (1.4104): EN 10088-3-2005 | ||||||
| C | Si | Mn | P | S | Cr | Mo |
| 0.1 - 0.17 | max 1 | max 1.5 | max 0.04 | 0.15 - 0.35 | 15.5 - 17.5 | 0.2 - 0.6 |
| Mechanical properties of steel X14CrMoS17 (1.4104) | ||||||
| Rm - Tensile strength (MPa) (+QT650) | 650-850 | |||||
| Rp0.2 0.2% proof strength (MPa) +QT650 | 500 | |||||
| A - Min. elongation at fracture (%) (+QT650) | 10月12日 | |||||
| Brinell hardness (HB): (+A) | 220 |
| EN 10088-3:2005不锈钢。一般用途耐腐蚀钢的半成品、棒材、线材、型材和光亮产品的交货技术条件 | ||||||||
| EN 10028-7:2007压力用钢制扁平产品。不锈钢 | ||||||||
| EN 10217-7:2005压力用焊接钢管。不锈钢管 | ||||||||
| EN 10253-3:2008对焊管件。无特殊检验要求的锻造奥氏体和奥氏体-铁素体（双相）不锈钢 | ||||||||
| EN 10253-4:2008对焊管件。有特殊检验要求的锻制奥氏体和奥氏体-铁素体（双相）不锈钢 | ||||||||
| EN 10088-1:2005不锈钢。不锈钢清单 | ||||||||
| EN 10088-5:2009不锈钢。建筑用耐腐蚀钢棒材、棒材、线材、型材和光亮产品的交货技术条件 | ||||||||
| EN 10088-4:2009不锈钢。建筑用耐腐蚀钢片/板和带材交货技术条件 | ||||||||
| Equivalent grades: | ||||||||
| Chemical composition % of steel X2CrNiMo18-15-4 (1.4438): EN 10088-2-2005 | ||||||||
| 特定的硫含量范围可以改善特定的财产。对于可加工性，建议并允许将硫含量控制在0.015%至0.030%之间。对于可焊性，建议并允许将硫含量控制在0.008%至0.030%之间。对于可极化性，建议将硫含量控制在最大0.015%。 | ||||||||
| 未经买方同意，不得故意将本表中未列出的元素添加到钢材中，除非对铸件进行精加工。 | ||||||||
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| max 0.03 | max 1 | max 2 | 13 - 16 | max 0.045 | max 0.015 | 17.5 - 19.5 | 3月4日 | max 0.11 |
| Mechanical properties of steel X2CrNiMo18-15-4 (1.4438) | ||||||||
| Rm - Tensile strength (MPa) (+A) | 500-720 | |||||||
| Rm - Tensile strength (MPa) (+AT) | 490-690 | |||||||
| Rp0.2 0.2% proof strength (MPa) (+A) | 200-240 | |||||||
| Rp0.2 0.2% proof strength (MPa) (+AT) | 220 | |||||||
| KV - Impact energy (J) transverse, (+A) | +20° | -196° | ||||||
| 60 | 60 | |||||||
| KV - Impact energy (J) longitud., (+A) | +20° | |||||||
| 100 | ||||||||
| A - Min. elongation at fracture (%) (+A) | 35-40 | |||||||
| A - Min. elongation at fracture (%) longitud., (+AT) | 35 | |||||||
| Brinell hardness (HB): (+A) | 215 | |||||||
| Brinell hardness (HB): (+AT) | 200 | |||||||